850度铝真空钎焊炉：低温真空钎焊炉型号

Low Temperature Vacuum Brazing Furnace
低温真空钎焊炉

Description 说明：

Low temperature vacuum brazing furnace widely used in aluminum fin type heat exchanger, car radiator, car air conditioning evaporator, condenser, radar network antenna and aluminum brazing products such as waveguide pipe and all kinds of aluminum welding parts. The welding temperature is under 700 Celsius degrees.
低温真空钎焊炉广泛应用于铝翅片式换热器、汽车散热器、汽车空调蒸发器、冷凝器、雷达网络天线和波导管等铝钎焊产品以及各种铝焊接部件。焊接温度低于700摄氏度。
Technical Parameter：

型号技术参数：

Model	Working Zone Size (W*H*L)	Max. Temperature	Ultimate Pressure	Temperature Uniformity	Loading Capacity
STR VBF669L-8	600*600*900mm	850℃	6.7*10-3Pa	±3℃	500Kg
STR VBF7710L-8	700*700*1000mm	850℃	6.7*10-3Pa	±3℃	700Kg
STR VBF8812L-8	800*800*1200mm	850℃	6.7*10-3Pa	±3℃	1000Kg
STR VBF9915L-8	900*900*1500mm	850℃	6.7*10-3Pa	±3℃	1200Kg
STR VBF121220L-8	1200*1200*2000mm	850℃	6.7*10-3Pa	±3℃	3000Kg
STR VBF121240L-8	1200*1200*4000mm	850℃	6.7*10-3Pa	±3℃	5000Kg
STR VBF131320L-8	1300*1300*2000mm	850℃	6.7*10-3Pa	±3℃	3500Kg
STR VBF131340L-8	1300*1300*4000mm	850℃	6.7*10-3Pa	±3℃	5500Kg
Remark: The working zone of equipment could be customized base on customer’s production.

低温真空钎焊炉是一种钎焊温度 ≤700 ℃(设计温度850 ℃)的专用真空炉,主要用于铝、铜及其合金等低熔点材料的洁净钎焊。

工作原理

炉膛先由机械泵+罗茨泵/扩散泵抽至 10?1～10?3 Pa 的真空度;

在保护性真空环境中将工件整体加热到 500-700 ℃,使预先放置的钎料熔化而基体不熔;

钎料在毛细作用下填满焊缝,保温一段时间后随炉冷却,完成无氧化、无气孔的高强度连接。

结构特征

双层层板炉壳:内胆不锈钢+外壁碳钢,通水冷却,表面温升 ≤30 ℃;

加热元件:Ni-Cr 电阻丝或 Fe-Cr-Al 丝,最高设计温度 850 ℃;

保温层:1200 ℃级陶瓷纤维板,热惯性小,升温/冷却快;

真空系统:二级旋片泵 + 罗茨泵(10?2 Pa 级);可选配扩散泵(10-3 Pa 级);

控温:PID/PLC 多段可编程,控温精度 ±1 ℃,升温速率 ≤20 ℃·min-1。

典型应用

铝质汽车散热器、暖通空调蒸发器/冷凝器;

铜-不锈钢混合结构的板式换热器、微波器件外壳;

航空航天铝蜂窝板、液冷板及电子封装盒体;

各类需要高洁净、无焊剂残留的低熔点金属钎焊场景。

低温真空钎焊炉真空度：铝钎焊通常 10⁻² Pa 已足够；若对色泽或高纯铜焊缝要求极高，可选配扩散泵组到 10⁻³ Pa。